Characterisation of the performance parameters of some new broadband glasses for Raman amplification

Résumé

New glasses which exhibit a broadband Raman spectral response have been prepared and characterised for their Raman cross section and gain performance. Results on three different glass compositions in the system [(100-x)NaPO3-xNa2B4O7]:TiO2/Nb2O5=1 are summarised. The impact on the Raman properties of changing the phosphorus to boron ratio while maintaining the TiO2/Nb2O5 molar ratio equal to one, was examined. Polarised spontaneous Raman measurements are presented, and a comparison between the experimentally obtained Raman gain coefficient and that predicted from spontaneous Raman cross section measurements is made. Results obtained show that these glasses exhibit similar or slightly higher Raman gain coefficients than that of SiO2, with a spectral bandwidth almost five times greater (sim1300 cm-1).

Domaines

Matériaux
Fichier principal
Vignette du fichier
2005-122_tap.pdf (354.5 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-00102038 , version 1 (13-02-2024)

Identifiants

  • HAL Id : hal-00102038 , version 1

Citer

Clara Rivero, Kathleen Richardson, Robert Stegeman, George Stegeman, Thierry Cardinal, et al.. Characterisation of the performance parameters of some new broadband glasses for Raman amplification. Glass Technology - European Journal of Glass Science and Technology Part A, 2005, 46 (2), pp.80-84. ⟨hal-00102038⟩

Collections

CNRS ICMCB
31 Consultations
2 Téléchargements

Partager

Gmail Facebook X LinkedIn More