Hidden hysteretic behavior of a paramagnetic iron(II) network revealed by light irradiation - Institut de chimie de la matière condensée de Bordeaux Accéder directement au contenu
Article Dans Une Revue European Journal of Inorganic Chemistry Année : 2017

Hidden hysteretic behavior of a paramagnetic iron(II) network revealed by light irradiation

Résumé

The paramagnetic coordination polymer [Fe(3phOH-trz){Pt(CN)4}].2H2O was obtained by reaction of iron(II) salt with the 4-(3-hydroxyphenyl)-1,2,4-triazole (3phOH-trz) ligand and a [Pt(CN)4]2- salt. Its structure consists in two dimensional {FePt(CN)4} layers linked by π-stacking interactions and a strong H-bonds network between water molecules and the hydroxyl group from the ligand. From the paramagnetic high spin (HS) state at 10 K, irradiation at 830 nm led to the fully low spin (LS) state, according to the reverse-LIESST process. Upon warming, this LS state undergoes a thermally induced spin transition to high spin around 105 K. This photoswitching process is reversible and the paramagnetic state can be recovered by a 510 nm light irradiation below 105 K. Moreover, a permanent irradiation (830 nm) revealed a hidden hysteresis loop of 37 K width. Photocrystallographic experiments did not evidence any structural phase transition upon excitation but underlined that the elastic frustration might be responsible for the inhibition of the spin crossover in this compound and allowed the observation of the hidden hysteresis loop.
Fichier principal
Vignette du fichier
2018-019.pdf (1.52 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-01629238 , version 1 (02-03-2021)

Identifiants

Citer

Mame Mguenar Ndiaye, Sébastien Pillet, El-Eulmi Bendeif, Mathieu Marchivie, Guillaume Chastanet, et al.. Hidden hysteretic behavior of a paramagnetic iron(II) network revealed by light irradiation. European Journal of Inorganic Chemistry, 2017, 3-4, pp.305-313. ⟨10.1002/ejic.201701098⟩. ⟨hal-01629238⟩
215 Consultations
73 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More