Formation of locked-lamellar grains in a slightly hypoeutectic Al-Al2Cu alloy during thin-sample directional solidification

Abstract

We studied the formation and growth of locked-lamellar microstructures in a thin sample of a slightly hypoeutectic Al-Al2Cu alloy. The coupled-growth dynamics, including early stages and steady-state regimes, was observed optically in real time during directional solidification. The orientation of the a (Al) and q (Al2Cu) crystals was measured ex situ in a series of eutectic grains by X-ray Laue microdiffraction. A nucleation event of a q crystal on a pre-existing a crystal, and the subsequent growth of a eutectic grain with a type-C orientation relationship, that is, with a coincidence of {123}-a and {100}-q planes, were observed in situ. In type-C eutectic grains, lamellar locking occurred parallel to the low-energy coincidence plane. A regular (floating) coupled-growth dynamics was observed in misoriented eutectic grains.
Fichier principal
Vignette du fichier
ICASP6_Proceedings_1_preprint.pdf (4.38 Mo) Télécharger le fichier
Origin : Files produced by the author(s)

Dates and versions

hal-03777032 , version 1 (14-09-2022)

Identifiers

  • HAL Id : hal-03777032 , version 1

Cite

M Medjkoune, S Bottin-Rousseau, L Carroz, G Prévot, B Croset, et al.. Formation of locked-lamellar grains in a slightly hypoeutectic Al-Al2Cu alloy during thin-sample directional solidification. 2022. ⟨hal-03777032⟩
78 View
21 Download

Share

Gmail Facebook Twitter LinkedIn More