Static and impact toughness properties of LB-PBF-built and heat treated 33CrMoV12 steel

Résumé

The mechanical properties of LB-PBF-build 33CrMoV12 steel grade were investigated for different material states (Asbuilt, tempered, double tempered and quenched-tempered) and discussed in relation to the inherited microstructures. As-built LB-PBF samples have higher tensile properties and lower impact toughness compared to the wrought material. A cellular microstructure was observed, consisting of martensite cells surrounded by nano-sized austenite. The presence of 25% of austenite is explained by a strong carbon segregation evidenced by high resolution SIMS (Secondary Ion Mass Spectroscopy). Further tempering causes an important drop in impact toughness. XRD showed that austenite was destabilized, forming brittle phases. Double tempering doesn't restore the impact toughness to the value of conventional material. Finally, austenite quenching and tempering allows to restore static and impact toughness similar to the value of conventional material, indicating a sufficient homogenization of the carbon microsegregations induced by fast solidification during LB-PBF process .
Fichier principal
Vignette du fichier
Mechanical properties of SLM-built and heat treated 33CrMoV12 steel in relation to the inherited microstructures_VF.pdf (756.45 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03918896 , version 1 (02-01-2023)

Identifiants

  • HAL Id : hal-03918896 , version 1

Citer

Hervé Nicolas, Lambert Romain, Nathalie Gey, Perroud Olivier, Slama Meriem Ben Haj, et al.. Static and impact toughness properties of LB-PBF-built and heat treated 33CrMoV12 steel. 2023. ⟨hal-03918896⟩
32 Consultations
50 Téléchargements

Partager

Gmail Facebook X LinkedIn More