Switching of the ion exchange behaviour of PEDOT thin films during a potential cycling: an electrochemical atomic force microscopy study

Résumé

Thickness variations of poly(3,4-ethylenedioxythiophene) (PEDOT) thin films placed under potential conditioning were measured with the help of electrochemical atomic force microscopy (EC-AFM). In this purpose, in-situ AFM operating in the contact mode was coupled with either cyclic voltammetry (CV) or advanced cyclic voltammetry (AdCV). A PEDOT functionnalized platinum electrode was used simultaneously as a sample for in-situ AFM measurements and a working electrode in a usual three electrode electrochemical setup. PEDOT films were electrodeposited with the help of the CV technique from lithium perchlorate aqueous solutions. From these EC-AFM investigations, brand new PEDOT films were found to be anion exchangers, in good agreement with conclusions of investigations reported in literature. Unexpectedly, PEDOT films having undergone a comprehensive electrochemical cycling (i.e. an electrochemical aging) in a potential range encompassing narrowly their redox process by using tens of CV or AdCV potential cycles behave as cation exchangers. Such observation strongly suggests that the electrochemo-mechanical and ion exchange behaviours of PEDOT can be both switched by simply using a potential cycling. Interestingly, the initial steps of this switching process were observed on a brand new PEDOT film during 26 consecutive CV scans. In the course of this process still ongoing at the end of the 26th cycle, a second swelling peak appears and grows progressively beside the initial swelling peak attributed to an anion exchange behaviour. This leads to a dual ion exchange behaviour for the resulting PEDOT film within the explored potential range. Indeed, this new swelling peak can be attributed to a cation exchange behaviour from the comparison of the potential dependant chronothicknograms and corresponding voltathicknograms with those obtained previously in this work.
Fichier principal
Vignette du fichier
Accepted Manuscript-Pailleret_2021.pdf (5.12 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03234656 , version 1 (25-05-2021)

Identifiants

Citer

Adrien Mocaër, Françoise Pillier, Alain Pailleret. Switching of the ion exchange behaviour of PEDOT thin films during a potential cycling: an electrochemical atomic force microscopy study. Electrochimica Acta, 2021, 389, pp.138651. ⟨10.1016/j.electacta.2021.138651⟩. ⟨hal-03234656⟩
67 Consultations
70 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More