Sintering behavior and microstructural evolution of NbC-Ni cemented carbides with Mo2C additions - Science et Ingénierie des Matériaux et Procédés Accéder directement au contenu
Article Dans Une Revue International Journal of Refractory Metals and Hard Materials Année : 2020

Sintering behavior and microstructural evolution of NbC-Ni cemented carbides with Mo2C additions

Résumé

The effect of Mo2C additions to a NbC-12vol%Ni-0.5vol%WC material on sintering at 1450 °C and on the resulting microstructure was investigated by replacing different amounts of NbC with Mo2C (0%, 3%, 6% or 9% in volume) and by performing interrupted tests at key temperatures (1080 °C, 1180 °C and 1320 °C). Chemical reactions and phase transformations were followed by Thermogravimetric Analysis (TGA) and sintering behavior by dilatometry. The microstructure was studied by Scanning and Transmission Electron Microscopy (SEM and TEM), Energy Dispersive Spectrometry (EDS) and X-ray diffraction (XRD). It is observed that Mo2C and WC particles, present at the onset of solid state sintering, delay the shrinkage of the material. An increase of hardness with Mo2C addition is measured, mainly due to grain refinement.

Domaines

Matériaux
Fichier principal
Vignette du fichier
Version 10 - Article Frittage - M Labonne_LQ.pdf (1.28 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02888643 , version 1 (03-07-2020)

Identifiants

Citer

Mathilde Labonne, Jean-Michel Missiaen, Sabine Lay, Nerea García, Olivier Lavigne, et al.. Sintering behavior and microstructural evolution of NbC-Ni cemented carbides with Mo2C additions. International Journal of Refractory Metals and Hard Materials, 2020, 92, pp.105295. ⟨10.1016/j.ijrmhm.2020.105295⟩. ⟨hal-02888643⟩
83 Consultations
131 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More