Microstructural, Compositional & Optical Characteristics of GaN Grown by MOVPE on ZnO Epilayers

Résumé

This article presents the results of microstructural, compositional, and optical characterization of GaN films grown on ZnO buffered c-sapphire substrates. Transmission electron microscopy showed epitaxy between the GaN and the ZnO, no degradation of the ZnO buffer layer, and no evidence of any interfacial compounds. Secondary ion mass spectroscopy revealed negligible Zn signal in the GaN layer away from the GaN∕ZnO interface. After chemical removal of the ZnO, room temperature (RT) cathodoluminescence spectra had a single main peak centered at ∼368nm (∼3.37eV), which was indexed as near-band-edge (NBE) emission from the GaN layer. There was no evidence of the ZnO NBE peak, centered at ∼379nm (∼3.28eV), which had been observed in RT photoluminescence spectra prior to removal of the ZnO.
Fichier principal
Vignette du fichier
Rogers2009.pdf (129.68 Ko) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-00448880 , version 1 (01-12-2021)

Identifiants

Citer

Dave J. Rogers, Ferecteh Hosseini-Teherani, Tarik Moudakir, Simon Gautier, François Jomard, et al.. Microstructural, Compositional & Optical Characteristics of GaN Grown by MOVPE on ZnO Epilayers. Journal of Vacuum Science & Technology B, Nanotechnology and Microelectronics, 2009, 27 (3), pp.1655-1658. ⟨10.1116/1.3137967⟩. ⟨hal-00448880⟩
54 Consultations
24 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More