Crystallographic structure of vanadium carbide precipitates in a model Fe-C-V steel

Daniel Acevedo-Reyes
  • Fonction : Auteur
  • PersonId : 877700

Résumé

The crystallographic structure of vanadium carbide precipitates in iron is investigated using High Resolution Transmission Electron Microscopy (HRTEM) and conventional Selected Area Diffraction (SAD) analysis. After a two steps precipitation treatment (10 hours at 700°C and 10 days at 800°C) and different annealing treatments (from 870°C to 920°C) performed on an ultra-pure Fe-V-C model alloy, carbides exhibit unambiguously the ordered monoclinic form V6C5. The often reported V4C3 structure, that refers to the pioneer work by Baker and Nutting [R. G. Baker and J. Nutting, Precipitation processes in steels (1959)] is not encountered in the present investigation. Reasons for this contradiction will be discussed, and the conclusion is drawn that no literature data is available to unambiguously support the existence of precipitates with the V4C3 structure.

Mots clés

Domaines

Matériaux
Fichier principal
Vignette du fichier
PEER_stage2_10.1080%2F14786430701753816.pdf (4.08 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-00513843 , version 1 (01-09-2010)

Identifiants

Citer

Thierry Epicier, Daniel Acevedo-Reyes, Michel Perez. Crystallographic structure of vanadium carbide precipitates in a model Fe-C-V steel. Philosophical Magazine, 2008, 88 (1), pp.31-45. ⟨10.1080/14786430701753816⟩. ⟨hal-00513843⟩
144 Consultations
1064 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More