Surface reactivity of hydroxyapatite nanocoatings deposited on iron oxide magnetic spheres toward toxic metals - CNRS - Centre national de la recherche scientifique Accéder directement au contenu
Article Dans Une Revue Journal of Colloid and Interface Science Année : 2014

Surface reactivity of hydroxyapatite nanocoatings deposited on iron oxide magnetic spheres toward toxic metals

Résumé

Hypothesis : Hydroxyapatite and magnetite are two environmentally-friendly mineral phases that have fruitful properties for remediation process. The formation of magnetic core@sorbent shell nanostructures should provide efficient materials for toxic metal removal from aqueous media. However the nanoscale confinement of hydroxyapatite may influence its reactivity. Experiments : Fe3O4@Hydroxyapatite nanocomposites were prepared by surface-controlled precipitation of hydroxyapatite layers from 10 nm to 150 nm in thickness on iron oxide spheres. The surface reactivity of the core–shell particles toward selected inorganic ions of environmental relevance (Pb(II), Y(III), Eu(III), Sb(III)) was studied by batch sorption experiments, X-ray diffraction and electron microscopy. Findings : The reactivity of the hydroxyapatite coating varied from partial cation exchange to dissolution/transformation of the shell. The nature and extent of the reactions depended significantly on the hydroxyapatite layer structure but was not significantly influenced by the magnetic core. These novel nanocomposites should be useful for environmental applications.

Domaines

Matériaux
Fichier principal
Vignette du fichier
Yang_2014_Surface_reactivity.pdf (788.54 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01136087 , version 1 (26-03-2015)

Identifiants

Citer

Huihui Yang, Sylvie Masse, Hao Zhang, Christophe Hélary, Laifeng Li, et al.. Surface reactivity of hydroxyapatite nanocoatings deposited on iron oxide magnetic spheres toward toxic metals. Journal of Colloid and Interface Science, 2014, 417, pp.1-8. ⟨10.1016/j.jcis.2013.11.031⟩. ⟨hal-01136087⟩
214 Consultations
610 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More