Factors affecting MoO42- inhibitor release from Zn2Al based layered double hydroxide and their implication in protecting hot dip galvanized steel by means of organic coatings.

Résumé

Zn2Al/-layered double hydroxide (LDH) with intercalated MoO42– was investigated as a potential source of soluble molybdate inhibitor in anticorrosion coatings for hot dip galvanized steel (HDG). The effect of solution pH, soluble chlorides, and carbonates on the release kinetics of the interleaved MoO42– ions from the LDH powder immersed in solutions containing different anions was studied by X-ray diffraction, in situ attenuated total reflectance infrared (ATR-IR) spectroscopy, and inductively coupled plasma atomic emission spectroscopy (ICP-AES). The effect of the solution composition on the total release and the release kinetics was demonstrated. Less than 30% of the total amount of the intercalated MoO42– was released after 24 h of the immersion in neutral 0.005–0.5 M NaCl and 0.1 M NaNO3 solutions whereas the complete release of MoO42– was observed after 1 h in 0.1 M NaHCO3 or Na2SO4 and in alkaline solutions. The in situ ATR-IR experiments and quantification of the released soluble species by ICP-AES demonstrated the release by an anion exchange in neutral solutions and by the dissolution of Zn2Al/-LDH in alkaline solutions. The anion exchange kinetics with monovalent anions was described by the reaction order n = 0.35 ± 0.05 suggesting the diffusion control; for divalent anions, n = 0.70 ± 0.06 suggested the control by a surface reaction. Dissolution of Zn from coated HDG with and without Zn2Al/-MoO42– fillers, leaching of MoO42– from the coating, and the electrochemical impedance spectroscopy response of the coated systems were measured during the immersion in 0.5 M NaCl solutions with and without 0.1 M NaHCO3. Without carbonates, the release of soluble MoO42– was delayed for 24 h with no inhibiting effect whereas with 0.1 M NaHCO3 the immediate release was accompanied by the immediate and strong inhibiting effect on Zn dissolution. The concept of controlling the inhibition performance of LDH hybrid coatings by means of the environment composition is discussed.

Domaines

Chimie
Fichier non déposé

Dates et versions

hal-01276535 , version 1 (19-02-2016)

Identifiants

Citer

V. Shkirskiy, P. Keil, H. Hintze-Bruening, F. Leroux, P. Vialat, et al.. Factors affecting MoO42- inhibitor release from Zn2Al based layered double hydroxide and their implication in protecting hot dip galvanized steel by means of organic coatings. . ACS Applied Materials & Interfaces, 2015, 7, pp.25180-25192. ⟨10.1021/acsami.5b06702⟩. ⟨hal-01276535⟩
80 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More