Investigation of mixed ionic/nonionic building blocks for the dual templating of macro-mesoporous silica - CNRS - Centre national de la recherche scientifique Accéder directement au contenu
Article Dans Une Revue Journal of Colloid and Interface Science Année : 2019

Investigation of mixed ionic/nonionic building blocks for the dual templating of macro-mesoporous silica

Résumé

Traditional porous monoliths Si(HIPE) (High Internal Phase Emulsion), prepared from the Tetradecyltrimethylammonium Bromide (TTAB)/dodecane/water system, offer high specific surface area, mainly due to microporosity. Aside, mesoporous materials SBA-15, prepared from Pluronic P123, have a high specific surface area, but are obtained as powder, which limits their applications. Starting from the mixed TTAB-P123 surfactant, it is expected to tune the mesoporosity of Si(HIPE), while keeping their monolithic character. The ternary TTAB/P123/water phase diagram was established by varying the weight ratio between these two surfactants. The micellar structure as well as the structural parameters of the liquid crystal domains were determined by SAXS (Small Angle X-ray Scattering). The effect of dodecane solubilization was also investigated and concentrated emulsions were formulated from the (P123/TTAB)/dodecane/ water systems. After this soft matter dedicated study, the acquired knowledge was transferred toward the hierarchical porous silica generations, where the sol-gel process is involved. Mixing P123 with TTAB, macro-mesoporous monolithic silica with an enhanced contribution of the specific surface area due to mesoporosity can be prepared. The variation of the TTAB/P123 weight ratio allows controlling the porosity at the mesoscale. Moreover, the macroporosity can be tuned by changing the preparation method, by mixing either the two micellar solutions or directly the two surfactants prior the emulsification process.
Fichier principal
Vignette du fichier
JCIS-18-4153R1-revised.pdf (1.87 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-01864773 , version 1 (19-02-2022)

Identifiants

Citer

Armand Roucher, Melanie Emo, François Vibert, Marie-José Stebe, Véronique Schmitt, et al.. Investigation of mixed ionic/nonionic building blocks for the dual templating of macro-mesoporous silica. Journal of Colloid and Interface Science, 2019, 533, pp.385 - 400. ⟨10.1016/j.jcis.2018.08.068⟩. ⟨hal-01864773⟩
109 Consultations
37 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More