Detwinning of hierarchically structured martensitic variants in a directionally solidified non-modulated Ni-Mn-Ga alloy under uniaxial loading - CNRS - Centre national de la recherche scientifique Accéder directement au contenu
Article Dans Une Revue Scripta Materialia Année : 2017

Detwinning of hierarchically structured martensitic variants in a directionally solidified non-modulated Ni-Mn-Ga alloy under uniaxial loading

Résumé

The detwinning evolution of hierarchically structured martensitic variants in a directionally solidified non-modulated Ni-Mn-Ga alloy has been investigated by applying uniaxial compression parallel to the parent [001]A orientation with a cumulative strain of 3%, 7.3% and 10%, respectively. After each compression, the crystallographic orientations are obtained by manually indexing the Kikuchi patterns and the corresponding twinning relationships between the variants are also calculated. The results indicate that for both the intra-plate major-minor variants and inter-plate major-major variants, the detwinning occurs on the twins with high Schmid factor, resulting in a martensite only composed of favorable variants with [110]NM orientation parallel to the compression direction.

Domaines

Matériaux
Fichier non déposé

Dates et versions

hal-01901132 , version 1 (22-10-2018)

Identifiants

Citer

Long Hou, Yanchao Dai, Yves Fautrelle, Zongbin Li, Zhongming Ren, et al.. Detwinning of hierarchically structured martensitic variants in a directionally solidified non-modulated Ni-Mn-Ga alloy under uniaxial loading. Scripta Materialia, 2017, 134, pp.85-90. ⟨10.1016/j.scriptamat.2017.02.045⟩. ⟨hal-01901132⟩