3D characterization of partially recrystallized Al using high resolution diffraction contrast tomography - CNRS - Centre national de la recherche scientifique Accéder directement au contenu
Article Dans Une Revue Scripta Materialia Année : 2018

3D characterization of partially recrystallized Al using high resolution diffraction contrast tomography

Tianbo Yu
  • Fonction : Auteur
Chaoling Xu
  • Fonction : Auteur
Yubin Zhang

Résumé

Synchrotron diffraction contrast tomography (DCT) is for the first time used to characterize recrystallized grains in partially recrystallized Al. The positions, orientations and 3D shapes of >900 recrystallized grains are reconstructed within a gauge volume. The results are compared with those obtained using electron backscattered diffraction based on a statistical analysis. It is found that recrystallized grains with size larger than 10 μm, corresponding to ~98% of the total recrystallized volume of the sample, are well characterized by DCT. The advantages of DCT for recrystallization studies and new possibilities with DCT on new generation synchrotron sources are discussed.

Dates et versions

hal-01916290 , version 1 (08-11-2018)

Licence

Paternité - Pas d'utilisation commerciale

Identifiants

Citer

Jun Sun, Tianbo Yu, Chaoling Xu, Wolfgang Ludwig, Yubin Zhang. 3D characterization of partially recrystallized Al using high resolution diffraction contrast tomography. Scripta Materialia, 2018, 157, pp.72-75. ⟨10.1016/j.scriptamat.2018.08.001⟩. ⟨hal-01916290⟩
35 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More