Green electroluminescence from radial m -plane InGaN quantum wells grown on GaN wire sidewalls by metal–organic vapor phase epitaxy - CNRS - Centre national de la recherche scientifique Accéder directement au contenu
Article Dans Une Revue ACS photonics Année : 2018

Green electroluminescence from radial m -plane InGaN quantum wells grown on GaN wire sidewalls by metal–organic vapor phase epitaxy

Akanksha Kapoor
Eric Gautier
  • Fonction : Auteur
  • PersonId : 846306
Catherine Bougerol
Bruno Gayral
François Vurpillot
Lorenzo Rigutti
J. Eymery

Résumé

We demonstrate green emission from InGaN/ GaN multiple quantum wells (MQWs) grown on m-plane sidewalls of GaN wires. To tune the emission wavelength, InGaN radial wells were grown by metal−organic vapor phase epitaxy (MOVPE) at decreasing temperatures ranging from 710 down to 620 °C to increase the In incorporation. A comprehensive investigation combining structural and optical analyses demonstrates that the green emission from the nonpolar m-plane wire sidewalls is achieved for the wells grown at 650 °C (namely, for 2.7 nm thick wells sandwiched by 11 nm thick GaN barriers). The observed emission wavelength of 500−550 nm is consistent with an average In-content of MQWs measured in the range of 24 ± 4% by energy dispersive X-ray (EDX) and atom probe tomography (APT). Single wires were electrically contacted and the green electroluminescence from m-plane facets was established on single wire-LED devices. This demonstrates the possibility to produce green emitters with core−shell wire LEDs elaborated by industrial and scalable MOVPE technique.
Fichier principal
Vignette du fichier
SubACSPhotoGreen emission-APL-VFavecfigures.pdf (10.02 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-01986657 , version 1 (19-09-2022)

Identifiants

Citer

Akanksha Kapoor, Nan Guan, Martin Vallo, Agnès Messanvi, Lorenzo Mancini, et al.. Green electroluminescence from radial m -plane InGaN quantum wells grown on GaN wire sidewalls by metal–organic vapor phase epitaxy. ACS photonics, 2018, 5 (11), pp.4330-4337. ⟨10.1021/acsphotonics.8b00520⟩. ⟨hal-01986657⟩
154 Consultations
20 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More