Area selective deposition of TiO 2 by intercalation of plasma etching cycles in PEALD process: A bottom up approach for the simplification of 3D integration scheme - CNRS - Centre national de la recherche scientifique Accéder directement au contenu
Article Dans Une Revue Journal of Vacuum Science & Technology A Année : 2019

Area selective deposition of TiO 2 by intercalation of plasma etching cycles in PEALD process: A bottom up approach for the simplification of 3D integration scheme

Résumé

A selective deposition process for bottom-up approach was developed in a modified plasma enhanced atomic layer deposition (PEALD) sequence. As a case study, a very standard PEALD TiO2 using organo-amine precursor and O2 plasma is chosen. The metal oxide selectivity is obtained on TiN versus Si-based surfaces by adding one etching/passivation plasma step of fluorine every n cycles in a PEALD-TiO2 process. Fluorine gas NF3 allows (1) to etch the TiO2 layer on Si, SiO2, or SiN surface while keeping few nanometers of TiO2 on the TiN substrate and (2) to increase the incubation time on the Si-based surface. Quasi-in situ XPS measurements were used to study the incubation time between Si/SiO2 substrates versus TiN substrate. Results show that Si–F bonds are formed on Si and lock the surface reactions. The effectiveness of this atomic layer selective deposition method was successfully tested on a 3D patterned substrate with the metal oxide deposited only at the edge of metal lines.
Fichier principal
Vignette du fichier
vallat2019.pdf (722.46 Ko) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-02108939 , version 1 (28-09-2022)

Identifiants

Citer

Rémi Vallat, Rémy Gassilloud, Olivier Salicio, Khalil El Hajjam, Gabriel Molas, et al.. Area selective deposition of TiO 2 by intercalation of plasma etching cycles in PEALD process: A bottom up approach for the simplification of 3D integration scheme. Journal of Vacuum Science & Technology A, 2019, 37 (2), pp.020918. ⟨10.1116/1.5049361⟩. ⟨hal-02108939⟩
96 Consultations
171 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More