Temperature dependence of the electrochemical behavior of the 690 Ni-base alloy between 25 and 325 °C

Résumé

The electrochemical behavior and the chemical composition of passive films formed on the Alloy 690 at room temperature in borate buffer solution (pH = 9.0) was studied with different techniques for two surface finishings. XPS and quantum yield measurements showed the presence of Ni and Cr oxides and hydroxides for passive films formed on both the as received and the mechanically polished one, whereas the presence of mixed spinel type Ni (1-x) Fe x Cr 2 O 4 was only observed on the as received material. Additionally, Electrochemical Impedance Spectroscopy (EIS) highlighted a higher corrosion resistance for the as received alloy in comparison with the mechanically polished alloy, which was linked to the chemical composition of the oxide film. Electrochemical measurements were performed before, during, and after oxidation of the Alloy 690 of Steam Generator (SG) tube of Pressurized Water Reactor (PWR) at high temperature and high pressure in the simulated primary circuit of PWR. At high temperature, the interface becomes electrochemically active yielding the precipitation of the corrosion products which form a few tens of nm thick diffusion barrier for the released metal cations. This overlayer is built on the top of a few nm thick, Cr rich inner layer at the alloy/oxide interface which was found to behave similarly to that initially formed at ambient temperature. It is concluded that high temperature oxidation in the static condition of an autoclave at 325°C does not promote a better passivation state than the one already existing initially.

Domaines

Autre
Fichier principal
Vignette du fichier
El Euch_2019_Version pour HAL.pdf (845.98 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02164590 , version 1 (25-06-2019)

Identifiants

Citer

Salma El Euch, Damien Bricault, Hubert Cachet, Eliane Sutter, Mai T T Tran, et al.. Temperature dependence of the electrochemical behavior of the 690 Ni-base alloy between 25 and 325 °C. Electrochimica Acta, 2019, 317, pp.509-520. ⟨10.1016/j.electacta.2019.05.131⟩. ⟨hal-02164590⟩
58 Consultations
46 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More