Chemical Ordering in Bimetallic FeCo Nanoparticles: From a Direct Chemical Synthesis to Application As Efficient High-Frequency Magnetic Material - CNRS - Centre national de la recherche scientifique Accéder directement au contenu
Article Dans Une Revue Nano Letters Année : 2019

Chemical Ordering in Bimetallic FeCo Nanoparticles: From a Direct Chemical Synthesis to Application As Efficient High-Frequency Magnetic Material

G. Viau

Résumé

Single crystalline FeCo nanoparticles with tunable size and shape were prepared by co-decomposing two metal-amide precursors under mild conditions. The nature of the ligands introduced in this organometallic synthesis drastically affects the reactivity of the precursors and thus the chemical distribution within the nanoparticles. The presence of the B2 short-range order was evidenced in FeCo nanoparticles prepared in presence of HDAHCl ligands, combining 57 Fe Mössbauer, zero field 59 Co Ferromagnetic Nuclear Resonance (FNR) and X-ray diffraction studies. This is the first time that the B2 structure is directly formed during synthesis without the need of any annealing step. The as-prepared nanoparticles exhibit magnetic properties comparable with the ones of the bulk (Ms = 226 Am².kg-1). Composite magnetic materials prepared from these FeCo nanoparticles led to a successful proof-of-concept of integration on inductor-based filters (27% enhancement of the inductance value at 100 MHz).
Fichier principal
Vignette du fichier
Publi FeCo-Garnero-2019.pdf (1.43 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-02165756 , version 1 (02-03-2021)

Identifiants

Citer

Cyril Garnero, Mathieu Lepesant, Cécile Marcelot, Yooleemi Shin, Christian Mény, et al.. Chemical Ordering in Bimetallic FeCo Nanoparticles: From a Direct Chemical Synthesis to Application As Efficient High-Frequency Magnetic Material. Nano Letters, 2019, 19 (2), pp.1379-1386. ⟨10.1021/acs.nanolett.8b05083⟩. ⟨hal-02165756⟩
103 Consultations
71 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More