Microstructural and mechanical investigation of the near fusion boundary region in thermally aged 18MND5 / Alloy 52 narrow-gap dissimilar metal weld - CNRS - Centre national de la recherche scientifique Accéder directement au contenu
Article Dans Une Revue Materials Science and Engineering: A Année : 2020

Microstructural and mechanical investigation of the near fusion boundary region in thermally aged 18MND5 / Alloy 52 narrow-gap dissimilar metal weld

Résumé

Detailed characterization of the near fusion-boundary region of 18MND5 / Alloy 52 dissimilar metal weld joints was performed to investigate the effect of thermal aging on the microstructure and mechanical properties and to quantify the diffusion of carbon into the weld metal. It was shown that the microstructural features of dissimilar metal welds, such as the size of the partially mixed zone in the weld and the adjacency to micro-segregations in the low-alloy steel have an effect on the peak carbon concentration in the enriched region of the weld. Aging conditions (time and temperature) influence the position of this concentration peak in the weld. Those trends were supported by thermodynamic calculations.
Fichier principal
Vignette du fichier
Dissimilar metal weld_accepted.pdf (1.49 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02733004 , version 1 (02-06-2020)

Identifiants

Citer

A. Akhatova, F. Robaut, M. Verdier, M. Yescas, F. Roch, et al.. Microstructural and mechanical investigation of the near fusion boundary region in thermally aged 18MND5 / Alloy 52 narrow-gap dissimilar metal weld. Materials Science and Engineering: A, 2020, 788, pp.139592. ⟨10.1016/j.msea.2020.139592⟩. ⟨hal-02733004⟩
82 Consultations
98 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More