Nickel platinum (Ni x Pt 1−x ) nanoalloy monodisperse particles without the core–shell structure by colloidal synthesis

Résumé

We report a new and versatile colloidal route towards the synthesis of nanoalloys with controlled size and chemical composition in the solid solution phase (without phase segregation such as core–shell structure or Janus structure) or chemical ordering. The principle of the procedure is based on the correlation between the oxidation–reduction potential of metal cations present in the precursors and the required synthesis temperature to nucleate particles without phase segregation. The procedure is demonstrated via the synthesis of Face Centered Cubic (FCC) NixPt1−x nanoparticles, which was elaborated by the co-reduction of nickel(II) acetylacetonate and platinum(II) acetylacetonate with 1,2-hexadecanediol in benzyl ether, using oleylamine and oleic acid as surfactants. The chemical composition and solid solution FCC structure of the nanoalloy are demonstrated by crosslinking imaging and chemical analysis using transmission electron microscopy and X-ray diffraction techniques. Whatever the chemical composition inspected, a systematic expansion of the lattice parameters is measured in relation to the respective bulk counterpart.
Fichier principal
Vignette du fichier
d0na00450b.pdf (2.42 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-02969101 , version 1 (06-01-2021)

Licence

Paternité

Identifiants

Citer

Cora Moreira da Silva, Armelle Girard, Maxime Dufond, Frédéric Fossard, Amandine Andrieux-Ledier, et al.. Nickel platinum (Ni x Pt 1−x ) nanoalloy monodisperse particles without the core–shell structure by colloidal synthesis. Nanoscale Advances, 2020, 2 (9), pp.3882-3889. ⟨10.1039/D0NA00450B⟩. ⟨hal-02969101⟩
81 Consultations
34 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More