Iron-rich clay mineral synthesis using design of experiments approach

Hella Boumaiza
  • Fonction : Auteur
Lionel Limousy
  • Fonction : Auteur
  • PersonId : 1052921
Christelle Martin
Nicolas Michau
  • Fonction : Auteur
Liva Dzene

Résumé

The precipitation of iron-rich clay minerals has been reported in various geologic environments. However, large quantities of these minerals are not widely accessible to study their thermodynamic properties and thus improve our understanding of these particular geological systems. To obtain sufficient amount of iron-rich minerals, their synthesis can be foreseen. A design of experiments and surface response methodology was used in this study to find optimum synthesis conditions for these clay minerals. Three parameters were considered: quantity of OH-, synthesis time and temperature. The quantity of OH- had the largest influence on the synthesis result. The amount of 2:1 type clay mineral with respect to 1:1 type clay mineral increased with OH/Fe molar ratio. Time and temperature had less significant impact on the synthesis outcome, yet the formation of 2:1 type phase was favored at short synthesis time (1 day) and high temperature (160°C). The findings suggested that the kinetic of 2:1 type clay mineral phase formation with respect to 1:1 type phase was faster, yet the precipitation was strongly dependent on the availability of the reactants.
Fichier principal
Vignette du fichier
islandora_105375.pdf (889 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02988894 , version 1 (04-11-2020)

Identifiants

Citer

Hella Boumaiza, Patrick Dutournie, Jean-Marc Le Meins, Lionel Limousy, Jocelyne Brendle, et al.. Iron-rich clay mineral synthesis using design of experiments approach. Applied Clay Science, 2020, 199, pp.105876. ⟨10.1016/j.clay.2020.105876⟩. ⟨hal-02988894⟩
31 Consultations
95 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More