Giant low-field magnetocaloric effect in Si alloyed Ni-Co-Mn-In alloys - CNRS - Centre national de la recherche scientifique Accéder directement au contenu
Article Dans Une Revue Scripta Materialia Année : 2019

Giant low-field magnetocaloric effect in Si alloyed Ni-Co-Mn-In alloys

Résumé

For NiMn-based Heusler alloys, simultaneously achieving high magnetization difference and low thermal hysteresis across the magnetostructural transformation is of crucial importance to obtain large low-field actuated magnetocaloric properties. Here, the fifth element Si was introduced to replace In for reducing the thermal hysteresis in Ni-Co-Mn-In alloys while keeping a large magnetization change through the martensitic transformation. Consequently, a giant maximum entropy change ΔSMmax of 33.6 J kg−1 K−1 under the low field change of 2 T was achieved in a Ni45Co5Mn37In12Si1 alloy, which is among the highest values reported in NiMn-based alloys.
Fichier non déposé

Dates et versions

hal-03080261 , version 1 (17-12-2020)

Identifiants

Citer

Zongbin Li, Shuya Dong, Zhenzhuang Li, Bo Yang, Fang Liu, et al.. Giant low-field magnetocaloric effect in Si alloyed Ni-Co-Mn-In alloys. Scripta Materialia, 2019, 159, pp.113-118. ⟨10.1016/j.scriptamat.2018.09.029⟩. ⟨hal-03080261⟩
27 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More