Hydrogen diffusion and trapping in a low copper 7xxx aluminium alloy investigated by Scanning Kelvin Probe Force Microscopy - CNRS - Centre national de la recherche scientifique Accéder directement au contenu
Article Dans Une Revue Materials Science and Engineering: A Année : 2017

Hydrogen diffusion and trapping in a low copper 7xxx aluminium alloy investigated by Scanning Kelvin Probe Force Microscopy

Résumé

The susceptibility to hydrogen embrittlement (HE) of the 7046 aluminium alloy (AA 7046) was investigated. Samples of AA 7046 corresponding to different ageing temperature/time couples were hydrogenated by cathodic charging in a H2SO4 solution. Scanning Kelvin Probe Force Microscopy (SKPFM) combined with global hydrogen amount measurements allowed apparent hydrogen diffusion coefficients (Dapp) to be measured: the decrease of the Dapp values with the increase of the ageing duration was attributed to hydrogen trapping by hardening η’ and η precipitates for the aged alloy. Additional SKPFM measurements were carried out on hydrogen charged samples after desorption at 25 °C and combined with SEM observations of the fracture surfaces after tensile tests. Results showed that hydrogen could be trapped at the grain boundaries leading to brittle intergranular fracture. However, hardening precipitates could act as efficient trapping sites and reduce hydrogen trapping at the grain boundaries. Conclusion is that the most critical microstructural parameters for HE of AA 7046 correspond to the grain boundaries while ageing could contribute to improve the resistance to HE of the alloy by a well-controlled precipitation.
Fichier principal
Vignette du fichier
19371_oger.pdf (1.33 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03222780 , version 1 (10-05-2021)

Identifiants

Citer

Loïc Oger, Manon Chloé Lafouresse, Grégory Odemer, Lionel Peguet, Christine Blanc. Hydrogen diffusion and trapping in a low copper 7xxx aluminium alloy investigated by Scanning Kelvin Probe Force Microscopy. Materials Science and Engineering: A, 2017, 706, pp.126-135. ⟨10.1016/j.msea.2017.08.119⟩. ⟨hal-03222780⟩
26 Consultations
64 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More