Comparative Investigation of Activated Carbon Electrode and a Novel Activated Carbon/Graphene Oxide Composite Electrode for an Enhanced Capacitive Deionization - CNRS - Centre national de la recherche scientifique Accéder directement au contenu
Article Dans Une Revue Materials Année : 2020

Comparative Investigation of Activated Carbon Electrode and a Novel Activated Carbon/Graphene Oxide Composite Electrode for an Enhanced Capacitive Deionization

Gbenro Folaranmi
  • Fonction : Auteur
  • PersonId : 1100323
Mikhael Bechelany
Philippe Sistat
Marc Cretin
  • Fonction : Auteur
  • PersonId : 753971
  • IdHAL : marc-cretin
Francois Zaviska

Résumé

Capacitive deionization is an emerging brackish water desalination technology whose principle lies in the utilization of porous electrodes (activated carbon materials) to temporarily store ions. Improving the properties of carbon material used as electrodes have been the focus of recent research, as this is beneficial for overall efficiency of this technology. Herein, we have synthesized a composite of activated carbon/graphene oxide electrodes by using a simple blending process in order to improve the hydrophilic property of activated carbon. Graphene oxide (GO) of different weight ratios was blended with commercial Activated carbon (AC) and out of all the composites, AC/GO-15 (15 wt.% of GO) exhibited the best electrochemical and salt adsorption performance in all operating conditions. The as prepared AC and AC/GO-x (x = 5, 10, 15 and 20 wt.% of GO) were characterized by cyclic voltammetry and their physical properties were also studied. The salt adsorption capacity (SAC) of AC/GO-15 at an operating window of 1.0 V is 5.70 mg/g with an average salt adsorption rate (ASAR) of 0.34 mg/g/min at a 400 mg/L salt initial concentration and has a capacitance of 75 F/g in comparison to AC with 3.74 mg/g of SAC, ASAR of 0.23 mg/g/min and a capacitance of 56 F/g at the same condition. This approach could pave a new way to produce a highly hydrophilic carbon based electrode material in CDI.

Domaines

Matériaux
Fichier principal
Vignette du fichier
Materials 2020, 13, 5185.pdf (5.3 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-03242865 , version 1 (31-05-2021)

Licence

Paternité

Identifiants

Citer

Gbenro Folaranmi, Mikhael Bechelany, Philippe Sistat, Marc Cretin, Francois Zaviska. Comparative Investigation of Activated Carbon Electrode and a Novel Activated Carbon/Graphene Oxide Composite Electrode for an Enhanced Capacitive Deionization. Materials, 2020, 13 (22), pp.5185. ⟨10.3390/ma13225185⟩. ⟨hal-03242865⟩
31 Consultations
55 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More