Cycloidal Magnetic Order Promoted by Labile Mixed Anionic Paths in M 2 (SeO 3 )F 2 (M = Mn 2+ , Ni 2+ ) - CNRS - Centre national de la recherche scientifique Accéder directement au contenu
Article Dans Une Revue Inorganic Chemistry Année : 2021

Cycloidal Magnetic Order Promoted by Labile Mixed Anionic Paths in M 2 (SeO 3 )F 2 (M = Mn 2+ , Ni 2+ )

Résumé

Two M2(SeO3)F2 fluoro-selenites (M = Mn 2+ , Ni 2+) have been synthesized using optimized hydrothermal reactions. Their 3D framework consists of 1D-[MO2F2] 4chains of edge-sharing octahedra with a rare topology of O-O and F-F alternating µ2 bridges. The inter-chain corner sharing connections are assisted by the mixed O vs. F anionic nature and develop a complex set of M-X-M super-exchanges calculated by LDA+U. Their interplay induce prominent in-chain antiferromagnetic frustration while the interchain exchanges are responsible for the cycloidal magnetic structure observed below TN ~21.5 K in the Ni 2+ case. For comparison the Mn 2+ compound develops a nearly collinear spin (canted) ordering below TN ~26 K with ferromagnetic chain-units.
Fichier principal
Vignette du fichier
Hall-M2(SeO3)F2 .pdf (1.09 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03300303 , version 1 (27-07-2021)

Identifiants

Citer

Tianyu Zhu, Olivier Mentré, Haoming Yang, Yong Jin, Xinan Zhang, et al.. Cycloidal Magnetic Order Promoted by Labile Mixed Anionic Paths in M 2 (SeO 3 )F 2 (M = Mn 2+ , Ni 2+ ). Inorganic Chemistry, 2021, 60 (16), pp.12001-12008. ⟨10.1021/acs.inorgchem.1c01074⟩. ⟨hal-03300303⟩
34 Consultations
90 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More