Nanoindentation study of hydride diffusion layer in commercial pure titanium - CNRS - Centre national de la recherche scientifique Accéder directement au contenu
Article Dans Une Revue Materials Science and Engineering: A Année : 2022

Nanoindentation study of hydride diffusion layer in commercial pure titanium

Résumé

In this work, the mechanical properties of hydride diffusion layer were thoroughly researched by nano indentation technique. For the first time, the clear section microstructure of hydride diffusion layer was revealed under scanning electron microscope with complicated interactions of hydride plates near the interface between hydride layer and titanium matrix. The hydride layer section has higher hardness and lower modulus towards titanium matrix due to the hard nature and easier crack nucleation of hydride precipitation. Besides, the hardness of titanium matrix shows considerable anisotropy. The anisotropic hardness of sample surface was studied before and after hydrogen charging. The hardness of titanium matrix decreases with the increase of deviation angle between c-axis and surface normal. The hydride layer formed in the titanium grain with more favorable orientation for hydride transformation tends to possess higher indentation hardness.
Fichier principal
Vignette du fichier
LEM3_MSEA_2022_.pdf (9.25 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03471263 , version 1 (08-12-2021)

Identifiants

Citer

Qian Wang, Jean-Sébastien Lecomte, Christophe Schuman, Laurent Peltier. Nanoindentation study of hydride diffusion layer in commercial pure titanium. Materials Science and Engineering: A, 2022, 832, pp.142428. ⟨10.1016/j.msea.2021.142428⟩. ⟨hal-03471263⟩
79 Consultations
35 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More