Defect Engineering of Monoisotopic Hexagonal Boron Nitride Crystals via Neutron Transmutation Doping

Christine Elias
  • Fonction : Auteur
  • PersonId : 1047974
Song Liu
  • Fonction : Auteur
Guillaume Cassabois
  • Fonction : Auteur
  • PersonId : 1002524
Bernard Gil
  • Fonction : Auteur
  • PersonId : 995090
Pierre Valvin
  • Fonction : Auteur
  • PersonId : 987631
Thomas Pelini
  • Fonction : Auteur
  • PersonId : 990942
Rui He
Bin Liu
  • Fonction : Auteur

Résumé

The nature of point defects in hexagonal boron nitride (hBN) is of current interest for the potential to alter its optical and electrical properties. The strong interaction between neutrons and the boron-10 isotope makes neutron irradiation a controllable way to introduce point defects in hBN. In this study, we perform Raman spectroscopy, photoluminescence, electron paramagnetic resonance (EPR), and optically detected magnetic resonance (ODMR) characterization of neutron-irradiated monoisotopic (hBN with a single boron isotope) 10 B-and 11 B-enriched hBN crystalline flakes and a pyrolytic BN (pBN) reference sample. In h 10 BN and pBN, neutron irradiation produced two new Raman bands at 450 and 1335 cm −1 , which could be associated with B-related vacancies or defects. The near-bandedge optical emission was also significantly impacted by the neutron irradiation. EPR measurements clarified the origin of a high-spin defect center due to negatively charged boron vacancies, which was recently reported for similar neutron-irradiated hBN crystals. The ODMR experiments further confirmed this assignment. High-temperature annealing partially recovered some of the hBN vibrational and optical properties. Our results are helpful to identify the nature of defects in hBN and enable defect-engineered applications such as quantum information and sensing.
Fichier non déposé

Dates et versions

hal-03674350 , version 1 (20-05-2022)

Identifiants

Citer

Jiahan Li, Evan R. Glaser, Christine Elias, Gaihua Ye, Dylan Evans, et al.. Defect Engineering of Monoisotopic Hexagonal Boron Nitride Crystals via Neutron Transmutation Doping. Chemistry of Materials, 2021, 33 (23), pp.9231-9239. ⟨10.1021/acs.chemmater.1c02849⟩. ⟨hal-03674350⟩
16 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More