Study of Deformation Mechanisms in Titanium by Interrupted Rolling and Channel Die Compression Tests

Résumé

The mechanisms of small plastic deformation of titanium (T40) during cold rolling and channel die compression by means of "interrupted in situ" EBSD orientation measurements were studied. These interrupted EBSD orientation measurements allow to determine the rotation flow field which leads to the development of the crystallographic texture during the plastic deformation. Results show that during rolling, tension twins and compression twins occur and various glide systems are activated, the number of grains being larger with twins than with slip traces. In channel die compression, only tension twins are observed in some grains, whereas slip traces can be spotted in almost all observed grains. The different stress conditions and different strain rates existing under the two modes of deformation lead to the activation of different deformation mechanisms.
Fichier principal
Vignette du fichier
cmc.2010.015.113.pdf (1.8 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-03864507 , version 1 (29-11-2022)

Identifiants

Citer

Lei Bao, Christophe Schuman, J.S. Lecomte, Marie Jeanne Philippe, Xiang Zhao, et al.. Study of Deformation Mechanisms in Titanium by Interrupted Rolling and Channel Die Compression Tests. CMC-Computers, Materials & Continua, 2022, 15 (2), pp.113-127. ⟨10.3970/cmc.2010.015.113⟩. ⟨hal-03864507⟩
35 Consultations
56 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More