Two new cubic perovskite oxides Ba3CoSb2O9 and Ba2SrCoSb2O9: Syntheses, crystal structures and magnetic properties - CNRS - Centre national de la recherche scientifique Accéder directement au contenu
Article Dans Une Revue Journal of Solid State Chemistry Année : 2023

Two new cubic perovskite oxides Ba3CoSb2O9 and Ba2SrCoSb2O9: Syntheses, crystal structures and magnetic properties

Résumé

Two new cubic perovskite oxides Ba3CoSb2O9 and Ba2SrCoSb2O9 were prepared and characterized. Ba3CoSb2O9 was prepared in polycrystalline form by high-pressure (HP) high-temperature treatment of the hexagonal 6H polytype of Ba3CoSb2O9. Polycrystalline samples of Ba2SrCoSb2O9 were obtained at ambient pressure by a solidstate reaction method. Combined Rietveld refinements of X-ray and neutron diffraction patterns indicated that HP Ba3CoSb2O9 and Ba2SrCoSb2O9 both crystallize in a Fm (3) over barm cubic double perovskite A(2)BB'O-6 structure with formulae Ba-2(Sb0.83Co0.17)(Co0.5Sb0.5)O-6 and (Ba1.33Sr0.67)Sb(Co0.7Sb0.3)O-6, respectively. Electron diffraction results obtained for Ba2SrCoSb2O9 showed no sign of additional periodicity. Weiss temperatures extracted from high-temperature magnetic susceptibility data were. theta approximate to -113 K and -118 K for HP Ba3CoSb2O9 and Ba2SrCoSb2O9, respectively. HP Ba3CoSb2O9 displays a weak ZFC-FC magnetic irreversibilty below 8 K. Ba2SrCoSb2O9 exhibits a spin freezing at T-f approximate to 6 K, and mu SR and Sb-121 NMR data revealed a magnetic transition towards a disordered ground state.
Fichier sous embargo
Fichier sous embargo
0 9 5
Année Mois Jours
Avant la publication
vendredi 3 janvier 2025
Fichier sous embargo
vendredi 3 janvier 2025
Connectez-vous pour demander l'accès au fichier

Dates et versions

hal-03920765 , version 1 (03-01-2023)

Identifiants

Citer

C. Darie, Pierre Bordet, Mélanie Viaud, Catherine Guillot-Deudon, Philippe Deniard, et al.. Two new cubic perovskite oxides Ba3CoSb2O9 and Ba2SrCoSb2O9: Syntheses, crystal structures and magnetic properties. Journal of Solid State Chemistry, 2023, 317, pp.123701. ⟨10.1016/j.jssc.2022.123701⟩. ⟨hal-03920765⟩
63 Consultations
10 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More