Easy preparation of small crystalline Pd 2 Sn nanoparticles in solution at room temperature - CNRS - Centre national de la recherche scientifique Accéder directement au contenu
Article Dans Une Revue Dalton Transactions Année : 2023

Easy preparation of small crystalline Pd 2 Sn nanoparticles in solution at room temperature

Résumé

We describe here a simple protocol yielding small (<2 nm) crystalline Pd2Sn nanoparticles (NPs) along with Pd homologues for sake of comparison. These NPs were obtained via an organometallic approach using Pd2(dba)3·dba (dba =dibenzylideneacetone) in THF with 2 equivalents of tributyltin hydride under 4 bars of H2 at room temperature. The Pd NPs homologues were prepared similarly, using Pd2(dba)3·dba with 2 equivalents of n-octylsilane. These NPs were found crystalline and very small with a similar mean size (ca. 1.5 nm). These NPs were finally used as nanocatalysts in solution for a benchmark Suzuki-Miyaura cross-coupling reaction. The Pd2Sn NPs were found more active than Pd NPs analogues, exhibiting remarkable performances with Pd loading as low as 13 ppb. This result demonstrates a beneficial effect of tin on palladium in catalysis.

Domaines

Chimie
Fichier principal
Vignette du fichier
accpeted article dalton Pd2Sn.pdf (3.34 Mo) Télécharger le fichier
Origine Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-03947028 , version 1 (19-01-2023)

Identifiants

Citer

Vincent Dardun, Tania Pinto, Loïc Benaillon, Laurent Veyre, Jules Galipaud, et al.. Easy preparation of small crystalline Pd 2 Sn nanoparticles in solution at room temperature. Dalton Transactions, 2023, ⟨10.1039/D2DT03476J⟩. ⟨hal-03947028⟩
39 Consultations
17 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More