Article Dans Une Revue Materials Letters Année : 2024

High temperature environmental scanning electron microscopy characterization of transient phase formation during conversion of simulated nuclear waste feed to glass

Résumé

In-situ High-Temperature Environmental Scanning Electron Microscopy (HT-ESEM) is used to characterize the transient phases formed during the melting of complex glass batch mixtures representing simulated nuclear waste feeds. The first phenomenon that occurs is the formation of oxyanionic salt melt, followed by the reaction of oxyanionic salts with refractory grains containing Si, Al, or Mg through surface reactions to form a molten alkali-alumino-boro-silicate phase. The onset temperatures of gas bubble formation and primary foaming are directly determined from the HT-ESEM measurements. The formation of sulfate lakes as well as the formation of high-temperature transient phases floating at the sample surface are also directly observed and identified. Convection currents are observed and their consequences on glass homogenization are discussed.

Fichier principal
Vignette du fichier
MLBLUE-D-24-03206-original.pdf (1.01 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)
Licence

Dates et versions

hal-04761232 , version 1 (31-10-2024)

Licence

Identifiants

Citer

Renaud Podor, J. Lautru, Richard Pokorný, Z. Nabyl, S. Schuller, et al.. High temperature environmental scanning electron microscopy characterization of transient phase formation during conversion of simulated nuclear waste feed to glass. Materials Letters, In press, ⟨10.1016/j.matlet.2024.137619⟩. ⟨hal-04761232⟩
91 Consultations
132 Téléchargements

Altmetric

Partager

  • More