Interpretation of Electrochemical Impedance for Corrosion of a Coated Silver Film in Terms of a Pore-in-Pore Model - Laboratoire Interfaces et Systèmes Electrochimiques Accéder directement au contenu
Article Dans Une Revue Journal of The Electrochemical Society Année : 2014

Interpretation of Electrochemical Impedance for Corrosion of a Coated Silver Film in Terms of a Pore-in-Pore Model

Résumé

Electrochemical impedance spectroscopy was used to study the degradation behavior of thin multilayer stacks; Si3N4/Ag/Si3N4. Measurements were carried out in 0.5 M Na2SO4 adjusted at pH 10. The impedance data collected at the open circuit potential were analyzed with a physical model where all elements are clearly defined. The results suggest a constant phase element behavior at the electrolyte dielectric interface assigned to an in-depth distribution of local resistivity through the dielectric layer induced by the electrolyte penetration. To explain the electrochemical behavior of the thin silver layer, a localized corrosion in a delaminated zone between the upper dielectric and the silver layers was adopted. The localized corrosion was found to be related to the granular structure of the silver layer in which pores are formed between the grains of silver. This model is equivalent to a recently developed double porosity or pore-in-pore model.

Domaines

Chimie Autre
Fichier principal
Vignette du fichier
manuscript Yasser-final_P1439.pdf (560.99 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01080922 , version 1 (01-07-2015)

Identifiants

Citer

Yasser Ben Amor, Eliane Sutter, Hisasi Takenouti, Mark E. Orazem, Bernard Tribollet. Interpretation of Electrochemical Impedance for Corrosion of a Coated Silver Film in Terms of a Pore-in-Pore Model. Journal of The Electrochemical Society, 2014, 161 (14), pp.C573-C579. ⟨10.1149/2.1151412jes⟩. ⟨hal-01080922⟩
268 Consultations
547 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More