The Role of Self‐Organized TiO 2 Nanotube Thickness on the Electrochemical Performance of Anodes for Li‐Ion Microbatteriess

Clement Ghigo
  • Fonction : Auteur
Hanna Sopha
  • Fonction : Auteur
Marcela Sepúlveda
  • Fonction : Auteur
Ludek Hromadko
  • Fonction : Auteur
Jhonatan Rodriguez-Pereira
  • Fonction : Auteur
Killian Dénoue
  • Fonction : Auteur
Jan Macak
  • Fonction : Auteur
Thierry Djenizian

Résumé

Self‐organized TiO 2 nanotube (TNT) layers with different thicknesses are prepared by anodization of Ti foils and then characterized by X‐ray diffraction (XRD), scanning electron microscopy (SEM), X‐ray photoelectron spectroscopy (XPS), and electrochemical techniques to be used as potential anodes for Li‐ion microbatteries. Electrochemical behaviors between 1 and 190 μm thick electrodes, which are the thickest ever studied layers as electrode, have been evaluated by cyclic voltammetry (CV) and chronopotentiometry at various kinetics. The highest areal capacity is obtained for TNT layers of 190 μm providing an initial discharge capacity of ≈5.3 mAh cm −2 at C/10. At faster kinetics, the ≈80 μm thick TNT layer reveals the best electrochemical behavior by offering 256 μAh cm −2 at 5 C and a good stability for 200 cycles at C/5. The influence of the increasing thickness on the electrochemical performance at fast rates can be attributed to the uncomplete reaction of TNT layers with Li ions and the enhancement of the formation of a solid electrolyte interphase. It is also shown that a very thick electrode is not able to sustain long and very fast cycles due to the mechanical deformations occurring during the successive insertion/extraction of Li ions.

Domaines

Chimie
Fichier principal
Vignette du fichier
2024_Energy Technology_Publi Clément_TiO2 Nt.pdf (3) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-04954134 , version 1 (18-02-2025)

Identifiants

Citer

Clement Ghigo, Hanna Sopha, Marcela Sepúlveda, Ludek Hromadko, Jhonatan Rodriguez-Pereira, et al.. The Role of Self‐Organized TiO 2 Nanotube Thickness on the Electrochemical Performance of Anodes for Li‐Ion Microbatteriess. Energy Technology, 2024, ⟨10.1002/ente.202400528⟩. ⟨hal-04954134⟩
0 Consultations
0 Téléchargements

Altmetric

Partager

More