MBE growth of Fe(211)/Au(110) multilayers on MgO(110) substrates
Résumé
A 0.9 nm-Fe(211)/3.1 nm-Au(110) superlattice has been grown and measured by SQUID magnetometry. The magnetization has been found in the plane and the easy direction is [011¯] due to tension strain along the [111¯] axis. A weak antiferromagnetic coupling across the Au layers (0.01 erg/cm2) has been deduced.