Microstructure investigation and flow behavior during thixoextrusion of M2 steel grade

Résumé

The microstructure investigation and flow behavior during thixoforging of M2 steel parts were investigated. Partial remelting was performed at processing temperatures ranging from 1290 ◦C to 1340 ◦C corresponding to a liquid fraction range between 10% and 30% (according to differential scanning calorimetry measurements and quantitative image analyses). A conventional microstructure for thixoforming process was obtained: spherical solid grains surrounded by liquid phase. The microstructure across the heated billets was relatively homogeneous with bigger grain size near the surface. Successful thixoextrusion for producing parts was finally achieved at processing temperatures. By investigating the microstructure and load-displacement curves, different mechanisms in various forming stages were proposed.
Fichier principal
Vignette du fichier
LCFC_JMPT_2015_GU.pdf (3.37 Mo) Télécharger le fichier
Format : typeAnnex_author
Loading...

Dates et versions

hal-01090603 , version 1 (03-12-2014)

Identifiants

Citer

Guochao Gu, Raphaël Pesci, Laurent Langlois, Eric Becker, Régis Bigot. Microstructure investigation and flow behavior during thixoextrusion of M2 steel grade. Journal of Materials Processing Technology, 2015, 216, pp.178-187. ⟨10.1016/j.jmatprotec.2014.09.009⟩. ⟨hal-01090603⟩
69 Consultations
373 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More