Synthesis and characterization of nanocomposite films consisting of TEMPO-oxidized nanocellulose / Graphene oxide - CNRS - Centre national de la recherche scientifique Accéder directement au contenu
Article Dans Une Revue Nashrieh Shimi va Mohandesi Shimi Iran Année : 2022

Synthesis and characterization of nanocomposite films consisting of TEMPO-oxidized nanocellulose / Graphene oxide

Résumé

In this study, films consisting of TEMPO-oxidized cellulose nanofibers (TOCNF) prepared from eucalyptus and graphene oxide (GO) were prepared by casting-evaporation method. The morphological structure, thermal stability and mechanical properties of the nanocomposite films were investigated by X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), thermogravimetric analysis (TGA) and tensile mechanical tests. The results obtained from the X-ray diffraction spectrum, FTIR spectrum and SEM observations revealed that TOCNF and graphene oxide were able to form nanocomposite films with homogeneous structure in low-weight percent of graphene oxide. Compared with films of Tempo-oxidized cellulose nanofibers (TOCNF/GO0%), the mean tensile strength of nanocomposite films consisted of 1.5 wt% of graphene oxide (TOCNF/GO1.5%) increased to 19%, which was not statistically significant. In addition, the mean tensile strength of nanocomposite films consisted of 3wt% of graphene oxide (TOCNF/GO3%) decreased to 14.5%, which was not statistically significant. The results of TGA showed that the thermal degradation temperature of TOCNF/GO0.5%, TOCNF/GO1.5% and TOCNF/GO3% nanocomposite films compared to the film of TOCNF/GO0% slightly changed towards lower temperatures.
Fichier non déposé

Dates et versions

hal-04099058 , version 1 (16-05-2023)

Identifiants

  • HAL Id : hal-04099058 , version 1

Citer

Hirsa Jouya Ardekani, Mohammad Talaeipour, Amirhooman Hemmasi, Behzad Bazyar, Alain Dufresne. Synthesis and characterization of nanocomposite films consisting of TEMPO-oxidized nanocellulose / Graphene oxide. Nashrieh Shimi va Mohandesi Shimi Iran, 2022. ⟨hal-04099058⟩

Collections

UGA CNRS LGP2
14 Consultations
0 Téléchargements

Partager

Gmail Facebook X LinkedIn More