La1.5Nd0.3Pr0.2NiO4.16: A wew cathode material for IT-Solid Oxide Fuel Cells - Institut de chimie de la matière condensée de Bordeaux Accéder directement au contenu
Article Dans Une Revue Electrocatalysis Année : 2023

La1.5Nd0.3Pr0.2NiO4.16: A wew cathode material for IT-Solid Oxide Fuel Cells

Résumé

The La1.5Nd0.3Pr0.2NiO4.16 material was prepared by the citrate method and used as a cathode for a solid oxide fuel cell (SOFC). The study was carried out in the presence of a thin interfacial layer composed of 50% GDC10 and 50% 8YSZ deposited on both surfaces of the GDC10 (Ce1.9Gd0.1O1.95) electrolyte. The purity of the materials was studied by X-ray diffraction, while X-ray photon-electron spectrometry (XPS) was used to characterize the surface chemical state of the synthesized material; the morphology of the electrode and cross-sectional images of the cell were obtained by scanning electron microscopy (SEM). Iodometric titration has also been performed to evaluate oxygen over-stoichiometry. Cross-sectional SEM images have shown good adherence between all the cell components, and the cationic character of the cathode material was confirmed by the XPS and iodometric analysis. The use of these materials as an oxygen cathode has shown interesting electrochemical properties with an area-specific resistance (ASR) value of the order of 0.060 (Ω.cm2) at 600 °C and 0.022 (Ω.cm2) at 700 °C. The activation energy (Ea) of the LNPNO5 material is very low and is of the order of 0.96 eV.
Fichier principal
Vignette du fichier
AmiraS_Electrocatalysis_2023_Submitted.pdf (1.04 Mo) Télécharger le fichier
AmiraS_Electrocatalysis_2023_Figures.pdf (1012.34 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-04027196 , version 1 (13-03-2023)

Identifiants

Citer

Sabah Amira, Mosbah Ferkhi, Fabrice Mauvy, Sébastien Fourcade, Jean-Marc. Bassat, et al.. La1.5Nd0.3Pr0.2NiO4.16: A wew cathode material for IT-Solid Oxide Fuel Cells. Electrocatalysis, 2023, 14 (4), pp.546-560. ⟨10.1007/s12678-023-00818-x⟩. ⟨hal-04027196⟩
51 Consultations
2 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More