Critical behavior and large magnetocaloric effect in La0.8K0.175Li0.025MnO3 nanopowder manganite

Résumé

The rhombohedral La0.8K0.175Li0.025MnO3 sample was elaborated using the sol–gel method at low temperature of 900 °C. The prepared sample exhibits a second-order paramagnetic-ferromagnetic transition with decreasing temperature. Based on the data of the magnetic measurements, the critical behavior analysis is investigated through various techniques such as modified Arrott plot, Kouvel–Fisher method and critical isotherm analysis. The critical exponents determined using the Kouvel-Fisher method are found to be = 0.533 and = 1.114 at ~ 270 K. The critical exponent values obtained are in agreement with the values predicted by the mean field model, indicating the existence of long-range magnetic interaction in our synthesized sample. The maximum of the magnetic entropy change is about 3.51 J kg−1 K−1 under a magnetic applied field change of 5 T. The relative cooling power is found to be 320.5 J kg−1 at 5 T. This value represents about 78% of that of standard gadolinium.
Fichier principal
Vignette du fichier
s10051-024-00846-6.pdf (2.14 Mo) Télécharger le fichier
Origine Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-04914091 , version 1 (27-01-2025)

Identifiants

Citer

Y. Regaieg, W. Cheikhrouhou-Koubaa, L. Sicard, E.K. Hlil. Critical behavior and large magnetocaloric effect in La0.8K0.175Li0.025MnO3 nanopowder manganite. The European Physical Journal B: Condensed Matter and Complex Systems, 2024, 97 (12), pp.204. ⟨10.1140/epjb/s10051-024-00846-6⟩. ⟨hal-04914091⟩
0 Consultations
0 Téléchargements

Altmetric

Partager

More