The environmental impact of plastic waste has been a real problem for the past decades. The incorporation of cleavable bonds in the polymer backbone is a solution to making a commodity polymer degradable. When radical polymerization is used, this approach is made possible by radical ring-opening polymerization (rROP) of a cyclic monomer that allows for the introduction of a weak bond into the polymer backbone. Among the various cyclic monomers that could be used in rROP, thionolactones are promising structures due to the efficiency of the C═S bond to act as a radical acceptor. Nevertheless, only a few structures were reported to be efficient. In this work, we used DFT calculations to gain a better understanding of the radical reactivity of thionolactones, and in particular, we focused on the transfer rate constant ktr value and its ratio with the propagation rate constant kp of the vinyl monomer. The closer to 1, the better is the statistical incorporation of the two comonomers into the backbone. These theoretical results were in good agreement with all of the experimental data reported in the literature. We thus used this approach to understand the key parameters to tune the reactivity of thionolactone to prepare random copolymers. We identified and prepared the 7-phenyloxepane-2-thione (POT) thionolactone that led to statistical copolymers with styrene and acrylate derivatives that were efficiently degraded under accelerated conditions (KOH in THF/MeOH, TBD in THF, or mCPBA in THF), confirming the theoretical approach. The compatibility with RAFT polymerization as well as the homopolymerization behavior of POT was established. This theoretical approach paves the way for the in-silico design of new efficient thionolactones for rROP.