Crystallographicandmagneticpropertiesof(Cu1 xVx)V2S4 (xE0.3) single crystals withthelayereddefectNiAsstructuresynthesizedunder high pressure - CNRS - Centre national de la recherche scientifique Accéder directement au contenu
Article Dans Une Revue Journal of Solid State Chemistry Année : 2011

Crystallographicandmagneticpropertiesof(Cu1 xVx)V2S4 (xE0.3) single crystals withthelayereddefectNiAsstructuresynthesizedunder high pressure

Résumé

We report on the reproducible growth of (Cu1−xVx)V2S4 single crystals of sizable dimensions (∼0.3 mm) and homogeneous composition (x≈0.3) by means of high-pressure synthesis. The refinement of single crystal X-ray diffraction data indicates that the crystal structure is of the monoclinic defect NiAs-type, which consists of a stacking of VS2 layers with CdI2-type structure and chains of edge-sharing (Cu1−xVx)S6 octahedra. Layers and chains form a network of face-sharing octahedra with no Cu–V intra-chain ordering. A combined X-ray photoelectron spectroscopy and bond valence sum analysis indicates that the valence of the V and Cu ions are 3+ and 1+, respectively. Magnetic susceptibility measurements unveil the coexistence of a large Pauli-like and of a small Curie-like paramagnetic contributions, with no evidence of any long range order down to 2 K. This result suggests a picture of predominantly itinerant 3d V electrons with significant electron–electron correlations.

Dates et versions

hal-00641600 , version 1 (16-11-2011)

Identifiants

Citer

Y. Klein, Hicham Moutaabbid, A. Soyer, M. d'Astuto, G. Rousse, et al.. Crystallographicandmagneticpropertiesof(Cu1 xVx)V2S4 (xE0.3) single crystals withthelayereddefectNiAsstructuresynthesizedunder high pressure. Journal of Solid State Chemistry, 2011, 184, pp.2333-2338. ⟨10.1016/j.jssc.2011.06.034⟩. ⟨hal-00641600⟩
124 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More