Etude electrochimique, et par microscopie electronique a balayage, du fer recouvert de peinture
Abstract
The authors first present results of observation, with a scanning electron microscope, of epoxy paint samples, deposited on iron or steel, which have undergone various types of attack (sulfuric acid medium, salt spray). This first part of the work shows that crevices and holes can be observed, penetrating the paint layer. The second part describes results obtained with electrochemical methods (polarization curves, complex interfacial electrode impedance diagrams, weight loss). These results show that the metal is corroded in the same way as when unprotected, but on a much reduced area, at the places where paint is lacking.
Les auteurs présentent d'abord des résultats d'observation, au microscope électronique à balayage, d'échantillons de peinture époxyde déposée sur du fer ou des aciers et ayant subi divers traitements agressifs (milieu sulfurique acide, brouillard salin). Cette première partie de l'étude montre qu'il peut exister des fissures, ou des trous traversant toute la couche de peinture. La seconde partie décrit les résultats obtenus par des méthodes électrochimiques (tracé de courbe courant-potentiel, mesures d'impédances complexes d'interface, pertes en poids de métal). Ces résultats montrent que le métal se corrode comme lorsqu'il est nu, mais sur une surface totale réduite, au droit des ruptures de continuité dans la couche de peinture.