Synergy effect between layer double hydroxide (LDH) and EDDS for corrosion inhibition of carbon steel

Résumé

Ethylenediamine-N,N’-disuccinate (EDDS) is successfully intercalated between layered double hydroxide (LDH) sheets leading to hybrid assembly [Zn2Al(OH)6]+ [EDDS]4- 0.25 2H2O (LDH-EDDS4-). The electrochemical behaviour of the carbon steel carried out in a neutral and aerated sodium chloride solution shows the surface reactivity of carbon steel is significantly decreased in presence of functionalized LDH-EDDS4-. To elucidate the inhibition mechanism provided by the hybrid assembly LDH-EDDS4-, each part constituting the funtionalized LDH is studied alone (Zn2+, Al3+ or EDDS4-) or in combination. A synergy effect between Zn2+ cations and EDDS4- anions is highlighted by anodic polarization and electrochemical impedance. In addition SEM and visual observations confirm the efficiency provided by the hybrid LDH-EDDS4- to protect carbon steel surface from corrosion.
Fichier principal
Vignette du fichier
Manuscript LDH-EDDS.pdf (1.56 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)
licence
Domaine public

Dates et versions

hal-04618874 , version 1 (20-06-2024)

Licence

Domaine public

Identifiants

  • HAL Id : hal-04618874 , version 1

Citer

Sabrina Marcelin, Gata Joseph Ayemi, Sandrine Therias, Leroux Fabrice, Bernard Normand. Synergy effect between layer double hydroxide (LDH) and EDDS for corrosion inhibition of carbon steel. 2024. ⟨hal-04618874⟩
0 Consultations
0 Téléchargements

Partager

Gmail Mastodon Facebook X LinkedIn More