Study on the thermal stability of Al/NbTiSiN/NbTiSiON/SiO2 solar selective absorbing coating.

Résumé

In this work, the NbTiSiN and NbTiSiON layers are used instead of NbTiN and NbTiON layers to further improve the thermal stability of Al/NbTiN/NbTiON/SiO2 multilayer solar selective absorbing coating. The thermal stability of Si-doped individual layers and multilayer coatings are investigated. The X-ray diffraction (XRD) results show that Si incorporation into NbTiN (NbTiSiN) layer does not change its preferred orientation, and the Si-doped NbTiON (NbTiSiON) layer remains in amorphous phase. On the other hand, by introducing Si into NbTiN and NbTiON layers induce significant improvement of the oxidation resistance at 500 °C in air. After ageing in air at 500 °C for 2 h, the absorptance and emittance (at 400 °C) of Al/NbTiN/NbTiON/SiO2 and Al/NbTiSiN/NbTiSiON/SiO2 multilayer coatings change from 0.934/0.13 and 0.931/0.12 to 0.538/0.14 and 0.922/0.13, respectively. Meanwhile the surface roughness increases from 18.3 and 7.9 to 41.5 and 14.7 respectively, as atomic force microscopy (AFM) shows. The Al/NbTiSiN/NbTiSiON/SiO2 coating still has a high absorptance (0.910) and low emittance (0.13, at 400 °C) after ageing at 550 °C in vacuum for 100 h. It displays that Si-doping play an important role in the improvement of the thermal stability.

Domaines

Chimie
Fichier non déposé

Dates et versions

hal-01214815 , version 1 (13-10-2015)

Identifiants

Citer

Yongxin Wu, Cong Wang, Ying Sun, Yuping Ning, Yingfang Liu, et al.. Study on the thermal stability of Al/NbTiSiN/NbTiSiON/SiO2 solar selective absorbing coating.. Solar Energy, 2015, 119, pp.18-28. ⟨10.1016/j.solener.2015.06.021⟩. ⟨hal-01214815⟩
219 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More