The High field magnetization of FePS 3

Résumé

High field magnetisation measurements in pulsed fields up to 65 Tesla have been performed on FePS3, which is nominally a good example of a two-dimensional Ising-like antiferromagnet on a honeycomb lattice. Measurements with the field parallel to the moment direction confirm the presence of two first-order transitions above 35 Tesla, to M/Msat = 1/2 and M/Msat = 1, respectively, at 4 K. The measurements are in contradiction with published estimates for the magnetic exchange parameters, but the contradiction can be resolved by allowing for anisotropic exchange parameters in the Hamiltonian. The magnetisation with the field perpendicular to the moment direction is anisotropic, with no transitions observed for fields along the a axis while a cascade of first-order transitions is observed for fields above 50 Tesla along the b axis, the latter case also showing a strong degradation of the sample after repeated pulses. The results indicate a strong magneto-lattice coupling in FePS3. Temperature-dependent measurements hint at a possible tricritical point.
Fichier principal
Vignette du fichier
FePS3_HiField_PRB_2.pdf (852.48 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03029896 , version 1 (29-11-2020)

Identifiants

Citer

A. R Wildes, D. Lançon, M. K Chan, F. Weickert, N. Harrison, et al.. The High field magnetization of FePS 3. Physical Review B, 2020, 101 (2), pp.024415. ⟨10.1103/PhysRevB.101.024415⟩. ⟨hal-03029896⟩
46 Consultations
197 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More