Flash spark plasma sintering of 3YSZ: Introducing structural and microstructural heterogeneity by high heating rates

Résumé

Yttria stabilized zirconia (3 mol% YSZ) ceramics were prepared by Flash-SPS at various temperatures ranging from 700° to 2060°C using heating rates ⁓11,000 °C/min, and leading to densification in seconds. The influence of peak temperature on microstructure is then analyzed and displays unusual sintering trajectory. Densification shows a maximum of 91 % around 1600 °C and further decreases with increasing sintering temperature. The structural and microstructural homogeneities are assessed, showing the presence of remaining monoclinic phase from starting powder in the core of the pellets, even after sintering at 2060 °C, suggesting strong thermal gradient. This also results in grain size and morphology heterogeneity. This work aims at showing the importance of assessing homogeneity over the whole sample volume, especially for ultra-rapid sintering techniques.
Fichier non déposé

Dates et versions

hal-04261419 , version 1 (27-10-2023)

Identifiants

Citer

Thomas Hérisson de Beauvoir, Elise Benard, Geoffroy Chevallier, Claude Estournès. Flash spark plasma sintering of 3YSZ: Introducing structural and microstructural heterogeneity by high heating rates. Journal of the European Ceramic Society, 2024, 44 (1), pp.579-584. ⟨10.1016/J.JEURCERAMSOC.2023.08.039⟩. ⟨hal-04261419⟩
22 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More