Martensite Decomposition and Ultrafine Grain Formation during Small Punch Creep Testing of Additively Manufactured Ti64 - CNRS - Centre national de la recherche scientifique
Journal Articles Metals Year : 2023

Martensite Decomposition and Ultrafine Grain Formation during Small Punch Creep Testing of Additively Manufactured Ti64

Abstract

The creep behaviour of as-built additive-manufactured Ti-6Al-4V alloy was studied through small punch creep test (SPCT) experiments at 450 and 500 °C. The couple stress/minimum strain rate deduced from these tests made it possible to draw a Norton plot showing good agreement with tensile test creep results. The microstructure characterisation within the SPCT specimen evidenced the effect of local strain on microstructure evolution. After interrupted creep at 450 °C, in most deformed areas, the as-built martensite structure was fully decomposed to the α + β equilibrium phases, giving rise to a submicron equiaxed grain structure.
Fichier principal
Vignette du fichier
Lale.pdf (2.97 Mo) Télécharger le fichier
Origin Publisher files allowed on an open archive
Licence

Dates and versions

hal-04261463 , version 1 (02-11-2023)

Licence

Identifiers

Cite

Mathieu Lalé, Benaissa Malek, Bernard Viguier. Martensite Decomposition and Ultrafine Grain Formation during Small Punch Creep Testing of Additively Manufactured Ti64. Metals, 2023, 13 (10), pp.1657. ⟨10.3390/MET13101657⟩. ⟨hal-04261463⟩
40 View
13 Download

Altmetric

Share

More