Photocatalytic Performance of Carbon-Containing CuMo-Based Catalysts under Sunlight Illumination - CNRS - Centre national de la recherche scientifique Accéder directement au contenu
Article Dans Une Revue Catalysts Année : 2022

Photocatalytic Performance of Carbon-Containing CuMo-Based Catalysts under Sunlight Illumination

Paula Muñoz-Flores
  • Fonction : Auteur
Po Poon
Catherine Sepulveda
  • Fonction : Auteur
Juan Matos

Résumé

Carbon-doped nanostructured CuMo-based photocatalysts were prepared by solvothermal synthesis. Two thermal treatments—oxidative and inert atmosphere—were used for the synthesis of the catalysts, and the influence of spherical carbon structures upon the crystalline phases on the photocatalytic activity and stability was studied. XRD showed the catalysts are nanostructured and composed by a mixture of copper (Cu, Cu2O, and CuO) and molybdenum (MoO2 and MoO3) crystalline phases. The catalysts were used for the degradation of yellow 5 under solar light. A remarkable leaching of Mo both in dark and under solar irradiation was observed and quantified. This phenomenon was responsible for the loss of photocatalytic activity for the degradation of the dye on the Mo-containing series. Conversely, the Cu-based photocatalysts were stable, with no leaching observed after 6 h irradiation and with a higher conversion of yellow 5 compared with the Mo- and CuMo series. The stability of Cu-based catalysts was attributed to a protective effect of spherical carbon structures formed during the solvothermal synthesis. Regarding the catalysts’ composition, sample Cu4-800-N2 prepared by pyrolysis exhibited up to 4.4 times higher photoactivity than that of the pristine material, which is attributed to a combined effect of an enhanced surface area and micropore volume generated during the pyrolytic treatment due to the presence of the carbon component in the catalyst. Scavenger tests have revealed that the mechanism for tartrazine degradation on irradiated Cu-based catalysts involves successive attacks of •OH radicals.
Fichier principal
Vignette du fichier
2022 MDPI Catalysts 12 (2022) 46_PMFlores.pdf (5.12 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03827360 , version 1 (24-10-2022)

Identifiants

Citer

Paula Muñoz-Flores, Po Poon, Catherine Sepulveda, Conchi Maria Concepcion Ovin Ania, Juan Matos. Photocatalytic Performance of Carbon-Containing CuMo-Based Catalysts under Sunlight Illumination. Catalysts, 2022, 12 (1), pp.46. ⟨10.3390/catal12010046⟩. ⟨hal-03827360⟩
9 Consultations
38 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More